Chemical and mechanical properties of Zirconia doping on glass ceramic - Zia, Rehana;Riaz, Madeeha
23,99 €
inkl. MwSt.

Versandfertig in 6-10 Tagen
payback
12 °P sammeln
  • Broschiertes Buch

Glass-ceramics in the SiO2-Al2O3-CaO-MgO system have been widely investigated for its various useful properties like low cost, superior mechanical strength, good chemical durability and excellent wear resistance. Diopside CaO-MgO- 2SiO2 crystalline phase generally precipitates in SiO2-Al2O3-CaO-MgO system which has desirable mechanical strength that may also be machined to some extent. Diopside (CaMgSi2O6) glassceramics are well known for their mechanical and electrical properties, i.e., high mechanical strength, low dielectric constant, high quality factor and low temperature sinterability.

Andere Kunden interessierten sich auch für
Produktbeschreibung
Glass-ceramics in the SiO2-Al2O3-CaO-MgO system have been widely investigated for its various useful properties like low cost, superior mechanical strength, good chemical durability and excellent wear resistance. Diopside CaO-MgO- 2SiO2 crystalline phase generally precipitates in SiO2-Al2O3-CaO-MgO system which has desirable mechanical strength that may also be machined to some extent. Diopside (CaMgSi2O6) glassceramics are well known for their mechanical and electrical properties, i.e., high mechanical strength, low dielectric constant, high quality factor and low temperature sinterability.
Autorenporträt
Prof. Dr.Rehana Zia was born in beautiful city of gardens i.e. ¿Lahore¿. She was born in 1960 in Lahore, Punjab and completed her entire education in Lahore. She did her M.Phil from Center of Solid State Physics, Punjab University in 1989. In 2009 she has completed her Ph.D in Physics