Andere Kunden interessierten sich auch für
![Effects of Prior Aging At 288°C in Argon Environment on Creep Response of Carbon Fiber Reinforced PMR-15 Composite with ±45° Fiber Orientation at 288°]( "Effects of Prior Aging At 288°C in Argon Environment on Creep Response of Carbon Fiber Reinforced PMR-15 Composite with ±45° Fiber Orientation at 288°")
Effects of Prior Aging At 288°C in Argon Environment on Creep Response of Carbon Fiber Reinforced PMR-15 Composite with ±45° Fiber Orientation at 288°60,99 €![Particulate Characterization and Control Evaluation for Carbon Fiber Composite Aircraft Crash Recovery Operations]( "Particulate Characterization and Control Evaluation for Carbon Fiber Composite Aircraft Crash Recovery Operations")
Particulate Characterization and Control Evaluation for Carbon Fiber Composite Aircraft Crash Recovery Operations60,99 €![Probabilistic Fiber Composite Micromechanics]( "Probabilistic Fiber Composite Micromechanics")
Probabilistic Fiber Composite Micromechanics60,99 €![Characterization of Graphite Composite Material Particulates from United States Air Force Aircraft Maintenance Operations]( "Characterization of Graphite Composite Material Particulates from United States Air Force Aircraft Maintenance Operations")
Characterization of Graphite Composite Material Particulates from United States Air Force Aircraft Maintenance Operations60,99 €![Effect of Temperature and Steam Environment on Fatigue Behavior of an Oxide-Oxide Continuous Fiber Ceramic Composite]( "Effect of Temperature and Steam Environment on Fatigue Behavior of an Oxide-Oxide Continuous Fiber Ceramic Composite")
Effect of Temperature and Steam Environment on Fatigue Behavior of an Oxide-Oxide Continuous Fiber Ceramic Composite60,99 €![An Evaluation of Organizational and Experience Factors Affecting the Perceived Transfer of U.S. Air Force Basic Combat Skills Training]( "An Evaluation of Organizational and Experience Factors Affecting the Perceived Transfer of U.S. Air Force Basic Combat Skills Training")
An Evaluation of Organizational and Experience Factors Affecting the Perceived Transfer of U.S. Air Force Basic Combat Skills Training60,99 €![Experimental Investigation of Jet Impingement Heat Transfer Using Thermochromic Liquid Crystals]( "Experimental Investigation of Jet Impingement Heat Transfer Using Thermochromic Liquid Crystals")
Experimental Investigation of Jet Impingement Heat Transfer Using Thermochromic Liquid Crystals60,99 €
The techniques necessary for the fabrication of a complex three-dimensional tubular form using a PMR-type resin have been developed to allow for the construction of several tubes with good physical and mechanical properties. Employing established resin transfer molding practices, the relatively non-hazardous AMB-21 in acetone formulation was used to successfully impregnate four layers of AS4 braided graphite fiber preform previously loaded around an aluminum cylindrical core in an enclosed mold cavity. Using heat and vacuum, the solvent was evaporated to form a prepreg followed by a partial imidization and removal of condensation products. The aluminum core was replaced by a silicone rubber bladder and the cure cycle continued to the final stage of 550 F with a bladder internal pressure of 200 lbs/sq in while simultaneously applying a strong vacuum to the prepreg for removal of any additional imidization products. A combination of several modifications to the standard resin transfer molding methodology enabled the mold to 'breathe', allowing the imidization products a pathway for escape. AMB-21 resin was chosen because of the carcinogenic nature of the primary commercial polyimide PMR-15. The AMB-21 resin was formulated using commercially available monomers or monomer precursors and dissolved in a mixture of methyl alcohol and acetone. The viscosity of the resulting monomer solution was checked by use of a Brookfield rheometer and adjusted by adding acetone to an easily pumpable viscosity of about 600 cP. In addition, several types of chromatographic and thermal analyses were of the braids, and excess handling of the preforms broke some of the microscopic fibers, needlessly decreasing the strength of the finished part. In addition, three dimensional braided preforms with fibers along the length of the tube will be significantly stronger in tension than the braided preforms used in this study.