Andere Kunden interessierten sich auch für
![Ion Implantation Synthesis and Optics of Metal Nanoparticles]( "Ion Implantation Synthesis and Optics of Metal Nanoparticles")
Ion Implantation Synthesis and Optics of Metal Nanoparticles38,99 €![Implantation Effect on GaSe Single Crystal]( "Implantation Effect on GaSe Single Crystal")
Implantation Effect on GaSe Single Crystal32,99 €![Surface Morphology & Structural studies on Materials by Implantation]( "Surface Morphology & Structural studies on Materials by Implantation")
Surface Morphology & Structural studies on Materials by Implantation46,99 €![Two-dimensional electron transport in GaN/GaAs based heterostructures]( "Two-dimensional electron transport in GaN/GaAs based heterostructures")
Two-dimensional electron transport in GaN/GaAs based heterostructures50,99 €![Theoretical Study of Electron Transport Characteristics in GaN]( "Theoretical Study of Electron Transport Characteristics in GaN")
Theoretical Study of Electron Transport Characteristics in GaN32,99 €![Controlled aggregation of Fe into GaN]( "Controlled aggregation of Fe into GaN")
Controlled aggregation of Fe into GaN26,99 €![Theoretical Study of Electrical Properties of n-type GaN]( "Theoretical Study of Electrical Properties of n-type GaN")
Theoretical Study of Electrical Properties of n-type GaN23,99 €
A detailed and systematic study of ion implanted MOCVD grown wurtzite gallium nitride (GaN) and aluminum indium nitride (AlInN) is conducted. As-grown samples were characterized using XRD and Hall measurements to check the structural and electrical properties of the samples. Neon (Ne), manganese (Mn) and cerium (Ce) ions were implanted into the materials with different doses in ranges 1014 9x1015, 1014 5x1016 and 3x1014 2x1015cm-2 respectively. Using rapid thermal annealing (RTA) furnace implanted GaN samples were annealed at 800, 850, 900 and 1000oC and implanted AlInN samples were annealed at 750 and 850 oC for lattice recovery and activation of the dopants. Structural and optical characterizations were made using Rutherford backscattering spectroscopy (RBS), X-Ray diffraction (XRD), Photoluminescence (PL), Optical transmission and Raman scattering spectroscopy. Moreover, magnetic characterization of Mn and Ce implanted samples was also carried out with vibrating sample magnetometer (VSM) and superconducting quantum interference device (SQUID).