Superconductors Material (Hg Family & Bi Family)

Preparation and Characterization of Superconductor Compounds M N Ca(n-1)Cu(n)O(x) M=(Hg, Bi2) N=(Ba2, Sr2)

• Broschiertes Buch

Produktbeschreibung

High temperature superconducting system Bi2Sr2Ca(n-1)Cu(n)O(2n+4+d) n=2,3,4 was prepared by using solid state reaction in oxygen. The nominal composition (n) has major effect on the critical temperature of superconductor compound. The sample prepared with n=2 has critical temperature Tc=104 K, meanwhile the sample prepared with n=4 has critical temperature Tc=86 K, however, the sample that was prepared with n=3 has a maximum critical temperature Tc=110 K. High temperature superconducting system HgBa2Ca(n-1)Cu(n)O(2n+2+d) n=2,3,4 was prepared by using sealed evacuate Quartz tube. The sample prepared with n=2 has critical temperature Tc=118 K, meanwhile the sample prepared with n=4 has critical temperature Tc=122 K, and for sample that was prepared with n=3 has a maximum critical temperature Tc=126 K

---

Hinweis: Dieser Artikel kann nur an eine deutsche Lieferadresse ausgeliefert werden.

Produktdetails

• Verlag: LAP Lambert Academic Publishing
• Seitenzahl: 132
• Erscheinungstermin: 19. Juni 2014
• Englisch
• Abmessung: 220mm x 150mm x 8mm
• Gewicht: 215g
• ISBN-13: 9783659557972
• ISBN-10: 3659557978
• Artikelnr.: 41154029

Autorenporträt

M.Sc in Material Science Solid State Physics/ Physics department/ college of Science/ Al-Nahrain University/ Baghdad- IraqI had awarded the B.Sc. degree in Physics, I had ranked (1) out of (11) students from the first turn through the academic year 2010 ¿ 2011. I completed the preparatory year in Master degree/I was ranked (1) out of (7)students