Andere Kunden interessierten sich auch für
![Prediction of Long-Term Strength of Thermoplastic Composites Using Time-Temperature Superposition]( "Prediction of Long-Term Strength of Thermoplastic Composites Using Time-Temperature Superposition")
Prediction of Long-Term Strength of Thermoplastic Composites Using Time-Temperature Superposition63,99 €![Effects of Prior Aging at Elevated Temperature in Air and in Argon Environments on Creep Response of PMR-15 Neat Resin at 288°C]( "Effects of Prior Aging at Elevated Temperature in Air and in Argon Environments on Creep Response of PMR-15 Neat Resin at 288°C")
Effects of Prior Aging at Elevated Temperature in Air and in Argon Environments on Creep Response of PMR-15 Neat Resin at 288°C63,99 €![The Effect of Elevated Temperature on the Fretting Fatigue Behavior of Nickel Alloy IN-100]( "The Effect of Elevated Temperature on the Fretting Fatigue Behavior of Nickel Alloy IN-100")
The Effect of Elevated Temperature on the Fretting Fatigue Behavior of Nickel Alloy IN-10064,99 €![Effects of Contact Load on the Fretting Fatigue Behavior of In-100 at Elevated Temperature]( "Effects of Contact Load on the Fretting Fatigue Behavior of In-100 at Elevated Temperature")
Effects of Contact Load on the Fretting Fatigue Behavior of In-100 at Elevated Temperature64,99 €![Characterization of Compressive Creep Behavior of Oxide/Oxide Composite with Monazite Coating at Elevated Temperature]( "Characterization of Compressive Creep Behavior of Oxide/Oxide Composite with Monazite Coating at Elevated Temperature")
Characterization of Compressive Creep Behavior of Oxide/Oxide Composite with Monazite Coating at Elevated Temperature64,99 €![Creep Performance of Oxide Ceramic Fiber Materials at Elevated Temperature in Air and in Steam]( "Creep Performance of Oxide Ceramic Fiber Materials at Elevated Temperature in Air and in Steam")
Creep Performance of Oxide Ceramic Fiber Materials at Elevated Temperature in Air and in Steam63,99 €![Rate-Dependence of Tensile Properties and Stress-Strain Behavior of an Oxide/ Oxide Ceramic Matrix Composite at Elevated Temperature and the Effects O]( "Rate-Dependence of Tensile Properties and Stress-Strain Behavior of an Oxide/ Oxide Ceramic Matrix Composite at Elevated Temperature and the Effects O")
Rate-Dependence of Tensile Properties and Stress-Strain Behavior of an Oxide/ Oxide Ceramic Matrix Composite at Elevated Temperature and the Effects O63,99 €
The magnitude of yield and flow stresses in aged Inconel 718 are observed to be different in tension and compression. This phenomenon, called the Strength differential (SD), contradicts the metal plasticity axiom that the second deviatoric stress invariant alone is sufficient for representing yield and flow. Apparently, at least one of the other two stress invariants is also significant. A unified viscoplastic model was developed that is able to account for the SD effect in aged Inconel 718. Building this model involved both theory and experiments. First, a general threshold function was proposed that depends on all three stress invariants and then the flow and evolution laws were developed using a potential-based thermodynamic framework. Judiciously chosen shear and axial tests were conducted to characterize the material. Shear tests involved monotonic loading, relaxation, and creep tests with different loading rates and load levels. The axial tests were tension and compression tests that resulted in sufficiently large inelastic strains. All tests were performed at 650 C. The viscoplastic material parameters were determined by optimizing the fit to the shear tests, during which the first and the third stress invariants remained zero. The threshold surface parameters were then fit to the tension and compression test data. An experimental procedure was established to quantify the effect of each stress invariant on inelastic deformation. This requires conducting tests with nonproportional three-dimensional load paths. Validation of the model was done using biaxial tests on tubular specimens of aged Inconel 718 using proportional and nonproportional axial-torsion loading. These biaxial tests also helped to determine the most appropriate form of the threshold function; that is, how to combine the stress invariants. Of the set of trial threshold functions, the ones that incorporated the third stress invariant give the best predictions.