Andere Kunden interessierten sich auch für
![Fretting Fatigue Behavior of a Titanium Alloy Ti-6AL-4V at Elevated Temperature]( "Fretting Fatigue Behavior of a Titanium Alloy Ti-6AL-4V at Elevated Temperature")
Fretting Fatigue Behavior of a Titanium Alloy Ti-6AL-4V at Elevated Temperature60,99 €![Analysis of Methods for Determining High Cycle Fatigue Strength of aA Material with Investigation of Ti-6Al-4V Gigacycle Fatigue Behavior]( "Analysis of Methods for Determining High Cycle Fatigue Strength of aA Material with Investigation of Ti-6Al-4V Gigacycle Fatigue Behavior")
Analysis of Methods for Determining High Cycle Fatigue Strength of aA Material with Investigation of Ti-6Al-4V Gigacycle Fatigue Behavior61,99 €![Creep Behavior of an Oxide/Oxide Composite with Monazite Coating at Elevated Temperatures]( "Creep Behavior of an Oxide/Oxide Composite with Monazite Coating at Elevated Temperatures")
Creep Behavior of an Oxide/Oxide Composite with Monazite Coating at Elevated Temperatures60,99 €![Consideration of Wear at High Velocities]( "Consideration of Wear at High Velocities")
Consideration of Wear at High Velocities60,99 €![The Effect of Microstructure on the Fretting Fatigue Behavior of Nickel Alloy IN-100]( "The Effect of Microstructure on the Fretting Fatigue Behavior of Nickel Alloy IN-100")
The Effect of Microstructure on the Fretting Fatigue Behavior of Nickel Alloy IN-10060,99 €![Fretting Fatigue Behavior of Shot-Peened IN 100]( "Fretting Fatigue Behavior of Shot-Peened IN 100")
Fretting Fatigue Behavior of Shot-Peened IN 10060,99 €![Houston, You Have a Problem: Will Manned Spaceflight Wear Out Its Welcome?]( "Houston, You Have a Problem: Will Manned Spaceflight Wear Out Its Welcome?")
Houston, You Have a Problem: Will Manned Spaceflight Wear Out Its Welcome?61,99 €
The effects of changes in the coefficient of friction (CoF) between the contacting surfaces on the fretting wear characteristics of Cu-Al coating on Ti-6Al-4V were investigated. This Cu-Al coating is part of a system that is applied to titanium turbine blades to reduce fretting at the interface. In the application, there is a solid lubricant that is added on top of the coating as an assembly aid and to help reduce the friction while the lubricant remains within the contact. Previous studies have researched the characteristics of the coating without the additional lubricant. In this study, liquid motor oil was applied to the contact region to simulate real-world conditions with a lower CoF. To characterize the wear, several methods were used, the most useful being the accumulated dissipated energy method.