M. Schutze

Protective Systems for High Temperature Applications EFC 57 (eBook, ePUB)

From Theory to Industrial Implementation

• Format: ePub

Produktbeschreibung

This book is a review of corrosion and thermal protection topics associated with coatings applied in high temperature applications, namely catalytic converters, combustion and steam environments, and gas turbines. Information on corrosion influencing mechanisms and their impact are reviewed.

---

Dieser Download kann aus rechtlichen Gründen nur mit Rechnungsadresse in A, B, BG, CY, CZ, D, DK, EW, E, FIN, F, GR, HR, H, IRL, I, LT, L, LR, M, NL, PL, P, R, S, SLO, SK ausgeliefert werden.

Produktdetails

• Verlag: Taylor & Francis
• Seitenzahl: 432
• Erscheinungstermin: 14. April 2023
• Englisch
• ISBN-13: 9781000950755
• Artikelnr.: 67738487

Autorenporträt

M. Schutze

Inhaltsangabe

Section 1: Aggressive Combustion Environments 1. Influence of novel cycle
concepts on the high temperature corrosion of power plants 2. Corrosion
behaviour of boiler steels, coatings and welds in flue gas environment 3.
Corrosion of alloys and their diffusion aluminide coatings by KCI:K2SO4
deposits at 650 °C in air 4. Oxide scale formation on Al containing
Ni-Cr-based high-temperature alloys during application as flame tube
material in recirculation oil burners 5. Development of thermally-sprayed
layers for high-temperature areas in waste incineration plants Section 2:
Steam Environments 6. High velocity oxy-fuel (HVOF) coatings for steam
oxidation protection 7. Identification of degradation mechanisms in
coatings for supercritical steam applications 8. Thermogravimetry-mass
spectrometry studies in coating design for supercritical steam turbines
Section 3: Catalytic Converters 9. Void formation and filling under alumina
scales formed on Fe-20Cr-5Al-based alloys and coatings, oxidised at
temperatures up to 1200 °C 10. Influence of a TiO2 surface treatment on the
growth and adhesion of alumina scales on FeCrAl alloys 11. A new austenitic
alumina forming alloy: Aluminium-coated FeNi32Cr20 Section 4: Gas Turbines
- Oxidation and Corrosion Protection 12. Effectiveness of platinum and
iridium in improving the resistance of Ni-Al to thermal cycling in
air-steam mixtures 13. Effect of manufacturing-related parameters on
oxidation properties of MCrAlY bond coats 14. Effect of creep-deformation
on oxidation behaviour of nickel-based alloy with a rhenium-based diffusion
barrier coating 15. Hot corrosion of coated and uncoated single crystal gas
turbine materials 16. Oxidation and alkali sulphate-induced corrosion of
aluminide diffusion coatings with and without platinum 17. Improving the
oxidation resistance of c-titanium aluminides by halogen treatment Section
5: Gas Turbines - Thermal Protection 18. Effect of surface preparation on
the durability of NiCoCrAlY coatings for oxidation protection and bond
coats for thermal barrier coatings 19. Parameters affecting the growth rate
of thermally grown oxides and the lifetime of thermal barrier coating
systems with MCrAlY bond coats 20. Influence of bond coat surface roughness
on chemical failure and delamination in thermal barrier coating systems 21.
Investigation on the oxidation behaviour of gamma titanium aluminides
coated with thermal barrier coatings 22. Role of bond coat depletion of
aluminium on the lifetime of air plasma sprayed thermal barrier coatings
under oxidising conditions 23. A software tool for lifetime prediction of
thermal barrier coating systems 24. Waste incineration corrosion processes:
Oxidation mechanisms by electrochemical impedance spectroscopy 25.
Behaviour of NiAl air plasma sprayed coatings in chlorine-containing
atmospheres 26. Parameters governing the reduction of oxide layers on
Inconel 617 in an impure VHTR He atmosphere 27. Protective coatings for
very high-temperature reactor applications 28. Oxidation of
electrodeposited Cr-C at temperatures between 400 °C and 900 °C in air 29.
Experimental analysis and computer-based simulation of nitridation of
Ni-Base alloys - the effect of a pre-oxidation treatment 30. Influence of
alloy compositions on the halogen effect in TiAl alloys 31. Modelling of
the long-term stability of the fluorine effect in TiAl oxidation 32.
High-temperature oxidation of Ti3Al0.7Si0.3C2 in air at 900 °C and 1000 °C